Zirconia based materials have been widely used in construction of dental prosthesis
because of their mechanical and aesthetical properties and a lot of money have been
invested in their development, but no one of the producers considered the aging of
zirconia. In this job have been demonstrated, with Raman spectroscopy, the low
temperature degradation of zirconia and has been investigated the residual stress in
zirconia-alumina composites at room temperature and in open-air after 8 years of
aging, then have been investigated the phase trasformation of tetragonal zirconia into
monocline form of pure zirconia and alumina-zirconia composites tested in water
with a thermal fatigue cycle between 5°C and 55°C. A partial solution of the problem
is proposed. Atomic Force Microsopy and Near-field Scanning Optical Microscopy
techniques have been tested as method of investigation and validation of the results. I materiali a base di zirconia trovano vasto impiego nella realizzazione di protesi
dentali grazie alle loro proprietà meccaniche ed estetiche e molti soldi sono stati
investiti nel loro sviluppo, ma nessuno dei produttori ha considerato il fenomeno di
invecchiamento della zirconia. In questo lavoro è stato dimostrato, attraverso
l‘impiego della spettroscopia Raman, il degrado a bassa temperatura della zirconia ed
è stato analizzato lo stato tensionale interno in compositi allumina-zirconia mantenuti
a temperatura ambiente in aria per 8 anni; a seguire è stata analizzata la
trasformazione di fase da tetragonale a monoclino della zirconia in campioni sia di
zirconia pura che in campioni di composito alumina-zirconia, testati in acqua e
sottoposti ad un ciclo di fatica termica tra 5°C e 55°C. Viene anche proposto un
metodo corretivo del problema. La microscopia a forza atomica e la microscopia ottica in campo prossimo sono state testate come strumento di verifica e validazione
dei dati ottenuti.